Authored by Usha Chowdhary
The study examined moisture management
behavior of plain, twill and satin weaves for 100% cotton. The intention
was to bridge the gap in
previous literature examined for the reported study. Increase in health
consciousness and fitness have increased demand for considering moisture
management research as we design apparel in the last twenty years.
Consumer has begun to value these attributes due to enhanced
expectations
of the textile and apparel consumers. Standardized tests from ASTM and
AATCC were performed to collect data. Date were analyzed using Analysis
of Variance (ANOVA) and t-test analysis. Confidence level of 95% was
established to test the hypotheses. The results revealed that three
weaves
differed for their wicking behavior, moisture transfer and water
repellency significantly. The findings could be explained based on
several structural
attributes. Some findings were consistent with the existing literature
and others were incongruent. Extension of work for future potential and
viability are discussed.
Introduction
Consumer values comfort in apparel and it can be determined by performance attributes such as horizontal wicking, moisture transfer, vertical wicking, and water repellency. Some work is published for the wicking behavior within the context of moisture management. Previous research studies compared different fiber content [1,2], direction [3,4], size of floats [5], different types of weaves [6,7], count, weight and porosity of fabric [8], texturizing of yarns [9], yarn size [10], and yarn type [11]. Moisture transfer and water repellency also impact body comfort. However, many studies were not found for them in literature. One study noted that water repellency of adding dendrimer to fluorocarbon remained the same [12]. Another investigation reported that adding mixed sol to nylon enhances its water and oil repellency [13]. Therefore, they were included for this study.Fabrics act differently before and after washing. All apparel goes through washing or dry cleaning for refurbishing. Several previous studies looked at the impact of washing on dimensional stability. However, very limited work is done for the wicking behavior [14,15]. Both of these studies investigated knitted fabrics.
None of the previous literature compared plain, twill and satin weaves. Because these are three basic weaves that are used to create other weaves, it was deemed important to examine their performance based on selected structural attributes. Impact of structural attributes was also reported in a limited manner.
Literature Review
Findings from the previous studies are reported to justify the developed hypotheses. One of the studies examined the wicking of Nylon 6.6 continuous and textured yarns. The authors found that tension applied to the twist impacted wicking significantly. Pore size and shape also had effect on wicking behavior [1]. Kundu SK, et al. [2] found that cotton and spandex blend had higher wicking rate than polyester/spandex and rayon/spandex. Another study reported that vertical wicking was higher in weft direction than warp direction [3]. They stressed to importance of fiber to fiber action as microcapillary and between yarn to yarn as microcapillary action. A team of scholars examined vertical wicking for cotton fabric and found that wicking rate was higher in weft than warp direction because number of yarns were more in the weft direction [4]. They recommended further research before generalizing any findings. Increase in percentage of floats and arcs increased the wicking behavior [5].A previous study that examined the same three weaves as used in the reported study but in different fiber contents found that warp cotton and weft polyester showed higher wicking height in warp of plain, twill and satin weaves [6]. Satin weave had higher wicking height in weft direction than twill and plain weaves. When both warp and weft were polyester, wicking rate was lower than the polyester blend. In their study, wicking increased from 5 minutes to 20 minutes. When warp was cotton and weft was polyester, higher wicking happened in warp because cotton has higher affinity to water. When warp was polyester and weft was cotton, higher wicking happened in the weft direction. When both warp and weft were polyester or poly/cotton blend, it showed higher absorption in twill and plain weaves. Parveen BK, et al. [7] used mercerized cotton and found that satin weave had higher wicking than twill and plain weaves. They attributed it to the longer floats. Another study reported on the impact of conventional and ring spun yarns on the wicking behavior of fabrics. Ring spun yarns performed better than the compact yarns [8]. Fabrics wicked similar to yarns. Mean for compact yarns was 3.99-4.35mm and that for ring yarns was 6.99mm after 20 minutes.
Another scholar found that change in fabric count, weight and porosity impacted the wicking ability of knitted fabrics. Increase in course density wicking increased and so was true for increase in porosity for vertical wicking [9]. A study of wicking of polyester unveiled that vertical wicking was influenced by the process to texturizing the yarn and fabric density in the weft direction [10]. The study did not find conclusive results for the weave type. However, texturized yarn had higher wicking rates than the filament yarns. Increase in number of yarns in crosswise direction, wicking height increased for 5-15 minutes and then stabilized. Moisture management study of profiled fabrics revealed that Viscose Outlast® provided the best wicking but low drying ability [11]. Coolmax® had good wicking and drying ability. Moisture management was weaker for coarser than finer fabrics. Increase in density resulted in increased thickness [3,11].
Adding dendrimer to fluorocarbon allowed same level of water repellency with less curing requirements [12]. Adding mixed solution to nylon was examined for its impact on water repellency [13]. Couple other studies examined the impact of laundering on wicking behavior of knitted fabrics and found that wicking improved between 5 and 25 study in one study and first to fifth wash in the other study [14,15]. Another study claimed that adding cotton to polyester increased dimensional instability of the fabric in both warp and weft directions. However, it was higher in widthwise than lengthwise direction [16]. Researchers examined that impact of physical factors on dimensional stability of cotton after repeated laundering. Several researchers purported that repeated laundering cycles increase shrinkage as well as fabric count, weight, thickness and cover factor [14,15,17]. One of the studies reported that the most change occurred until the fourth laundering [17,18] and another study noticed change beyond the fifth laundering for the knitted t-shirts [14]. Changes in weight, count and thickness can impact number of pores in a fabric and thus influence the wicking ability, wettability and moisture transfer of the fabric.
Based on the preceding literature review, following six hypotheses were developed.
Hypotheses
Based on the literature review, the following seven hypotheses were developed.Hypothesis 1: Three weaves will differ for horizontal wicking, moisture transfer, vertical- wicking, and water repellency in unwashed and washed forms.
Hypothesis 2: No difference will exist between three weaves for fabric thickness in washed and unwashed forms.
Hypothesis 3: Bleached and unbleached cotton in plain weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in unwashed and washed forms.
Hypothesis 4: High count bleached plain weave and satin weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency for washed and unwashed forms.
Hypothesis 5: Yarn size will impact horizontal and vertical wicking in washed and unwashed forms.
Hypothesis 6: Satin weave will have higher wicking than the plain and twill weaves due to longer floats.
Hypothesis 7: Fabric with plied yarns will have lower wicking than the single spun yarns.
Materials and Methods
This section defines attributes (Table 1), provides standards (Table 2), and describes methods used for this investigation. To establish common understanding, Table 2 provides information on the methods used to perform various tests for data collection. Table 2 also provide source for those tests, as well as number and size of specimens so that future researchers can replicate the work on other types of fabrics. Three fabrics were obtained from Cotton Incorporated. Plain cotton was received in the bleached form, and twill and satin were unbleached. To have valid comparison unbleached cotton was purchased from the local fabric store.
Structural Attributes
For fabric count, five places were selected across the width
and number of warp and weft were counted in both washed and
unwashed forms for plain, twill and satin fabrics (ASTM D 3775
-2017. They were reported using convention of warp x weft is equal
to warp + weft (Table 3-4) for both washed and unwashed forms.
Fabrics were then classified as medium (twill) and high (plain and
satin)20. Means and standard deviations were computed to allow
comparison for various variables using ANOVA and t-test analysis
at 95% level of confidence.
Fabric thickness was measured using ASTM D 1777-2015 using digital thickness tester. Thickness was measured at 5 places and means and standard deviation were calculated for subsequent analysis to test hypothesis related to this variable. Data are presented in tables 3&4. Fabric weight was determined by using ASTM D 3776-2002. Five specimens of 5”x5” dimensions were measured in both washed and unwashed forms. The following formula was used to calculate grams per square meter (GSM) and subsequent classification [20].
Grams per square meter (GSM ) = 33.906 x Ounces Per Square Yard
Three of the four fabrics were light weight and twill was heavy weight. Next, yarn size was measured using direct method in Tex unit. Tex refers to weight in grams of 1000 meters of yarn. Researchers weighed one meter of yarn and multiplied it by 1000 to compute as Tex. Standard did not explain it specifically. Therefore, it was performed using Chowdhary U [22]. ASTM test # D2260-03 (Reapproved 2013) offers conversion factors for changing from one system to another. The yarns were classified using Collier, et al. [23] as fine, medium and heavy.
Fabric weave and repeat were determined using linen tester [24]. All fabrics were woven fabrics. Plain weaves had 1x1 repeat. Repeat for the twill weave was 3x1 and for satin weave was 4x1. Previous researchers noted that float size can impact wicking [5]. Therefore, it was important to consider so.
Mean and standard deviations were computed for appropriate comparisons to determine statistical significance at 95% level of confidence. Information is provided in tables 3&4.
Moisture transfer was measured using AATCC 79 - 201425. Five specimens were collected from a framed fabric of 8”x8”. One drop of water was dispensed from 1inch height and time taken to absorb the drop was recorded for each observation in seconds. The maximum time allowed for the experiment was 60 seconds. Means and Standard deviations were computed for each weave and used for appropriate comparisons in both washed and unwashed forms (Tables 5&6).
Vertical wicking was tested using AATCC 197–2013 and lengthwise spread was measured in millimeters/second for both washed and unwashed specimens in three weaves. Data were collected and recorded using appropriate descriptive statistic for subsequent use in statistical analysis. Water Repellency was measured using AATCC 22-201425. Five specimens were used and 250ml water was sprayed on the specimen. Water pattern was compared to the replica and evaluated on at rating scale of 0-100 for each specimen in washed and unwashed forms. A minimum rating of 70 was classified as pass and below 70 as fail (Tables 5&6). Statistical analyses were used to test hypotheses.
To compare unwashed with washed specimens, the fabric was laundered using AATCC Laboratory Procedure 1-2018. A large piece of fabric was washed and then cut into recommended size of specimens for testing by the standardized tests used for the study.
For moisture transfer, Unbleached plain weave had higher moisture transfer than twill and stain weave in unwashed form Bleached cotton had higher moisture transfer than unbleached cotton for plain weave. Based on the standard of <5 seconds, only plain weave for bleached cotton passed in the washed form. However, all failed in the unwashed stage.
Results from Analysis of Variance and t-test were used to test hypothesis. Results were compared with previous research if available. For unwashed and washed forms exclusively and inclusively for three different weaves (Tables 5&6). For water repellency, all passed except the bleached plain weave. However, in washed farm, all failed except the twill weave.
Hypothesis 1: Three weaves will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in unwashed and washed forms.
Results revealed that three weaves differed significantly (Table 7) for horizontal wicking in the unwashed form (F2, 12= 1739.577. p<.05). So was true for the washed form (F2, 12= 655.619 p<.05). The t – value of comparison between unwashed and washed forms was also significant based on the t-test for all three weaves. Table 8 shows inter weave differences and reflects that differences were significant between Plain and twill, twill and satin, and sating and plain weaves for both conditions. Except for satin pattern was similar for the vertical wicking. Moisture transfer was significantly higher for washed form than unwashed form. However, inter-weave comparisons were significant for P x T and S x P for the unwashed form and P x T and T x S for the washed form. They were not significant for T x S in unwashed setting and S x P for the washed form. For water repellency, no change was observed for twill weave. However, post-wash ratings were significantly different for water repellency. Inter weave comparison by t-test revealed that the change was not significantly different for T x S in unwashed form, and S x P for the washed form. Overall, Hypothesis 1 was accepted. Figure 1 shows pictorial; depiction of relations between weaves and four performance attributes.
Hypothesis 2: No difference will exist between three weaves for fabric thickness in washed and unwashed forms.
ANOVA results revealed that Laundering made cotton fabric thicker than before for all three weaves (Table 9). Inter-weave comparisons also projected the same pattern. I could be function of residue left from detergent and potential shrinkage [14,15]. Hypothesis 2 was rejected. Pictorial depiction shows that thickness increased aster washing (Figure 2).
Table 9: Comparison between plain x twill, twill x satin, and satin x plain in washed and unwashed forms for fabric thickness.
Hypothesis 3: Bleached and unbleached cotton in plain weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in unwashed and washed forms.
The t-test analysis revealed that bleached cotton had better horizontal wicking, vertical wicking and moisture transfer than the unbleached cotton (Table 10). However, the unbleached cotton performed better on water repellency. When compared for washed and unwashed form, differences were significant for horizontal and vertical wicking, and as well as moisture transfer. However, differences were not significant for water repellency. Hypothesis 3 was accepted. Results makes sense because increase in moisture management is likely to have reduced water repellency. Pictorial description through Figure 3 also visually reflect so.
Hypothesis 4: High count bleached plain weave and satin weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in washed and unwashed forms.
Based on the statistical analysis, bleached plain cotton performed better for horizontal wicking, vertical wicking and moisture transfer than satin weave (Table 11). However, satin performed better on water repellency. Hypothesis 4 was accepted. Figure 4 visually demonstrates so. This finding is inconsistent with the previous study which found that satin weave has higher wicking because of longer floats [5]. They are also different from another research study which found that satin weave had higher wicking than both plain and twill weave [7].
Hypothesis 5: Yarn size will impact horizontal and vertical wicking in washed form.
The t-test analysis unveiled that wicking was higher for yarns in medium rather than heavy Yarn size (Table 12). Hypothesis 5 was accepted. Figure 5 reflects so too for yarn size in washed form for both types wicking. None of the previous study discussed this. Therefore, no comparison could be made with prior work.
Hypothesis 6: Satin weave will have higher wicking than the plain and twill weaves due to longer floats in washed form.
Based on ANOVA, this hypothesis was refuted. Plain weave had higher wicking than the satin weave (Table 12). Figure 5 attests so. Further work is needed before generalizing the outcome of this study because conflicting results.
Hypothesis 7: Fabric with plied yarns (twill weave) will have lower wicking than the single spun yarns (Plain and Satin weaves).
Twill weave that had plied yarn was compared with plain and satin weaves that had single spun yarns. The t-test analysis that compared twill weave with plain (bleached), plain unbleached and satin weaves. Results revealed that both plain and stain weaves with single spun yarn had significantly higher horizontal wicking than the twill weave. Hypothesis 7 was accepted. Since twill weave involves two twisting operations than plain and satin that were result of one twisting operation. Consequently, twill weave had more crystalline than amorphous region. Amorphous regions are likely to absorb higher moisture than crystalline regions [24]. Therefore, this finding has support from the previous literature [25,26].
Compare garments from various vistas of life to enhance understanding compatibility of textiles for diversified end uses as viable option.
Following questions may serve as the guiding force in accomplishing the proposed goal.
1. What is the role of various fiber contents and finishes with enhancing moisture management capability of textile materials and apparel made thereafter?
2. How layered and unlayered fabrics compare for the wicking behavior and moisture transfer?
3. In which other area can we cross apply the findings from the reported study?
4. What is the relationship between wicking behavior and thermal insulation?
5. How antimicrobial finishes support or challenge comfort, care and durability issues?
6. Should manufacturers consider pre-washing textiles before changing to garments because post-laundering performance was better than the unwashed form?
https://irispublishers.com/jtsft/fulltext/pre-post-wash-wicking-behavior-moisture-transfer-and-water-repellency-of-plain-twill-and-satin-weaves.ID.000539.php
Fabric thickness was measured using ASTM D 1777-2015 using digital thickness tester. Thickness was measured at 5 places and means and standard deviation were calculated for subsequent analysis to test hypothesis related to this variable. Data are presented in tables 3&4. Fabric weight was determined by using ASTM D 3776-2002. Five specimens of 5”x5” dimensions were measured in both washed and unwashed forms. The following formula was used to calculate grams per square meter (GSM) and subsequent classification [20].
Grams per square meter (GSM ) = 33.906 x Ounces Per Square Yard
Three of the four fabrics were light weight and twill was heavy weight. Next, yarn size was measured using direct method in Tex unit. Tex refers to weight in grams of 1000 meters of yarn. Researchers weighed one meter of yarn and multiplied it by 1000 to compute as Tex. Standard did not explain it specifically. Therefore, it was performed using Chowdhary U [22]. ASTM test # D2260-03 (Reapproved 2013) offers conversion factors for changing from one system to another. The yarns were classified using Collier, et al. [23] as fine, medium and heavy.
Fabric weave and repeat were determined using linen tester [24]. All fabrics were woven fabrics. Plain weaves had 1x1 repeat. Repeat for the twill weave was 3x1 and for satin weave was 4x1. Previous researchers noted that float size can impact wicking [5]. Therefore, it was important to consider so.
Performance attributes
Horizontal Wicking used AATCC 198 – 2013 for data collection [19]. Five specimens were cut in 8”x8” dimension. One cubic centimeter water was dispensed on a framed fabric with 1” difference between the tip of the burette and fabric surface. The dispensed water was left for five minutes and spread in length and width were measured in millimeters. Following formula was used to determine horizontal wicking in mm2/second.Mean and standard deviations were computed for appropriate comparisons to determine statistical significance at 95% level of confidence. Information is provided in tables 3&4.
Moisture transfer was measured using AATCC 79 - 201425. Five specimens were collected from a framed fabric of 8”x8”. One drop of water was dispensed from 1inch height and time taken to absorb the drop was recorded for each observation in seconds. The maximum time allowed for the experiment was 60 seconds. Means and Standard deviations were computed for each weave and used for appropriate comparisons in both washed and unwashed forms (Tables 5&6).
Vertical wicking was tested using AATCC 197–2013 and lengthwise spread was measured in millimeters/second for both washed and unwashed specimens in three weaves. Data were collected and recorded using appropriate descriptive statistic for subsequent use in statistical analysis. Water Repellency was measured using AATCC 22-201425. Five specimens were used and 250ml water was sprayed on the specimen. Water pattern was compared to the replica and evaluated on at rating scale of 0-100 for each specimen in washed and unwashed forms. A minimum rating of 70 was classified as pass and below 70 as fail (Tables 5&6). Statistical analyses were used to test hypotheses.
To compare unwashed with washed specimens, the fabric was laundered using AATCC Laboratory Procedure 1-2018. A large piece of fabric was washed and then cut into recommended size of specimens for testing by the standardized tests used for the study.
Results and Discussion
Results from the structural attributes revealed that bleached cotton had plain weave with fine yarn size, single spun yarn type, high count, light weight, and 1x1 repeat. Unbleached plain weave fabric had medium yarn size, single yarn, light weight and 1X1 repeat. Twill weave had heavy yarn size, plied yarn, medium count, heavy weight and 3x1 repeat. Finally, satin weave had medium yarn size, single yarn type, high count, light weight and 4x1 repeat. Fabric thickness was highest for twill weave followed by satin, unbleached plain, and bleached plain in both washed and unwashed forms. See tables 3&4. It was also observed that fabric thickness was higher in washed as opposed to the unwashed form for all weaves.Performance attributes
In general, means for beached and unbleached cotton in plain weave were higher than the twill and satin weave for horizontal wicking in both warp and weft directions in unbleached forms. This is finding is consistent with the result of previous study [8]. Bleached cotton had higher horizontal wicking than the unbleached cotton. The ratings of woven cotton for horizontal wicking were less than reported in the Technical Manual of the American Association of Textile Chemists and Colorist. Similar pattern was found for the vertical wicking.For moisture transfer, Unbleached plain weave had higher moisture transfer than twill and stain weave in unwashed form Bleached cotton had higher moisture transfer than unbleached cotton for plain weave. Based on the standard of <5 seconds, only plain weave for bleached cotton passed in the washed form. However, all failed in the unwashed stage.
Results from Analysis of Variance and t-test were used to test hypothesis. Results were compared with previous research if available. For unwashed and washed forms exclusively and inclusively for three different weaves (Tables 5&6). For water repellency, all passed except the bleached plain weave. However, in washed farm, all failed except the twill weave.
Hypothesis Testing
Based on the literature review, the following seven hypotheses were developed.Hypothesis 1: Three weaves will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in unwashed and washed forms.
Results revealed that three weaves differed significantly (Table 7) for horizontal wicking in the unwashed form (F2, 12= 1739.577. p<.05). So was true for the washed form (F2, 12= 655.619 p<.05). The t – value of comparison between unwashed and washed forms was also significant based on the t-test for all three weaves. Table 8 shows inter weave differences and reflects that differences were significant between Plain and twill, twill and satin, and sating and plain weaves for both conditions. Except for satin pattern was similar for the vertical wicking. Moisture transfer was significantly higher for washed form than unwashed form. However, inter-weave comparisons were significant for P x T and S x P for the unwashed form and P x T and T x S for the washed form. They were not significant for T x S in unwashed setting and S x P for the washed form. For water repellency, no change was observed for twill weave. However, post-wash ratings were significantly different for water repellency. Inter weave comparison by t-test revealed that the change was not significantly different for T x S in unwashed form, and S x P for the washed form. Overall, Hypothesis 1 was accepted. Figure 1 shows pictorial; depiction of relations between weaves and four performance attributes.
Hypothesis 2: No difference will exist between three weaves for fabric thickness in washed and unwashed forms.
ANOVA results revealed that Laundering made cotton fabric thicker than before for all three weaves (Table 9). Inter-weave comparisons also projected the same pattern. I could be function of residue left from detergent and potential shrinkage [14,15]. Hypothesis 2 was rejected. Pictorial depiction shows that thickness increased aster washing (Figure 2).
Table 9: Comparison between plain x twill, twill x satin, and satin x plain in washed and unwashed forms for fabric thickness.
Hypothesis 3: Bleached and unbleached cotton in plain weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in unwashed and washed forms.
The t-test analysis revealed that bleached cotton had better horizontal wicking, vertical wicking and moisture transfer than the unbleached cotton (Table 10). However, the unbleached cotton performed better on water repellency. When compared for washed and unwashed form, differences were significant for horizontal and vertical wicking, and as well as moisture transfer. However, differences were not significant for water repellency. Hypothesis 3 was accepted. Results makes sense because increase in moisture management is likely to have reduced water repellency. Pictorial description through Figure 3 also visually reflect so.
Hypothesis 4: High count bleached plain weave and satin weave will differ for horizontal wicking, moisture transfer, vertical wicking, and water repellency in washed and unwashed forms.
Based on the statistical analysis, bleached plain cotton performed better for horizontal wicking, vertical wicking and moisture transfer than satin weave (Table 11). However, satin performed better on water repellency. Hypothesis 4 was accepted. Figure 4 visually demonstrates so. This finding is inconsistent with the previous study which found that satin weave has higher wicking because of longer floats [5]. They are also different from another research study which found that satin weave had higher wicking than both plain and twill weave [7].
Hypothesis 5: Yarn size will impact horizontal and vertical wicking in washed form.
The t-test analysis unveiled that wicking was higher for yarns in medium rather than heavy Yarn size (Table 12). Hypothesis 5 was accepted. Figure 5 reflects so too for yarn size in washed form for both types wicking. None of the previous study discussed this. Therefore, no comparison could be made with prior work.
Hypothesis 6: Satin weave will have higher wicking than the plain and twill weaves due to longer floats in washed form.
Based on ANOVA, this hypothesis was refuted. Plain weave had higher wicking than the satin weave (Table 12). Figure 5 attests so. Further work is needed before generalizing the outcome of this study because conflicting results.
Hypothesis 7: Fabric with plied yarns (twill weave) will have lower wicking than the single spun yarns (Plain and Satin weaves).
Twill weave that had plied yarn was compared with plain and satin weaves that had single spun yarns. The t-test analysis that compared twill weave with plain (bleached), plain unbleached and satin weaves. Results revealed that both plain and stain weaves with single spun yarn had significantly higher horizontal wicking than the twill weave. Hypothesis 7 was accepted. Since twill weave involves two twisting operations than plain and satin that were result of one twisting operation. Consequently, twill weave had more crystalline than amorphous region. Amorphous regions are likely to absorb higher moisture than crystalline regions [24]. Therefore, this finding has support from the previous literature [25,26].
Summary and Conclusion
To summarize, wicking and moisture transfer were better for washed than unwashed forms for all weaves. Wicking was highest for the plain weave followed by satin and twill weave. Yarn size, yarn type, weave type, thickness, and fabric count. impacted the wicking behavior. Bleached cotton had better wicking than the unbleached cotton. Contrasting findings were found for wicking behavior and water repellency. This study controlled for fiber content and varied for the fabric construction. It also focused on other structural attributes to explain the findings. Analyses included comparisons among and between variables. Though not hypothesized, differences about impact of weight can also be eyeballed through analysis.Implications for Future
Due to increased demand for better moisture management, it has become imperative to compare performance of textiles available in the market for its appropriateness for the intended use and compatibility with multiple fiber contents and fabrics used in layered garments [27]. With increased blending of various fiber contents for enhanced comfort and performance makes it more important than ever before to make it their high priority because moisture management also impacts care and comfort. Extending this work to other fiber contents, fabric constructions, fabrics with different types of finishes, and other structural and performance attributes will enhance the reservoir of information base that can benefit future scholars and practitioners in the industry.Compare garments from various vistas of life to enhance understanding compatibility of textiles for diversified end uses as viable option.
Following questions may serve as the guiding force in accomplishing the proposed goal.
1. What is the role of various fiber contents and finishes with enhancing moisture management capability of textile materials and apparel made thereafter?
2. How layered and unlayered fabrics compare for the wicking behavior and moisture transfer?
3. In which other area can we cross apply the findings from the reported study?
4. What is the relationship between wicking behavior and thermal insulation?
5. How antimicrobial finishes support or challenge comfort, care and durability issues?
6. Should manufacturers consider pre-washing textiles before changing to garments because post-laundering performance was better than the unwashed form?
Acknowledgement
None.Conflict of Interest
No conflict of interest.
To read more about this article....Open access Journal of Textile Science & Fashion Technology