Authored by Mohamed Gouda*,
Abstract
Nickel oxide-carboxymethyl cellulose (NiO-CMC) nanocomposite was synthesized by the co-precipitation method to remove the methylene blue (MB) dye from wastewater. The synthesized nanocomposite was characterized by Fourier transform infrared spectroscopy (FT-IR), Scanning electron microscope (SEM), Energy dispersive X-ray analysis (EDX), Transmission electron microscope (TEM) as well as X-ray diffraction (XRD). Different factors such as the effect of the initial dye concentration, contact time, temperature, nanocomposite concentration, and pH parameters were investigated, and the obtained data showed that the optimum conditions to remove the MB were 3 mg/L, 4 hrs, 65 ∘C, 8 mg and pH 6, respectively. Furthermore, the adsorption kinetics, equilibrium isotherms, and thermodynamic were investigated, and data were agreed with the pseudo-secondorder equation and Langmuir model, respectively. Moreover, ΔSo, ΔHo, and ΔGo were calculated, and the results were indicated that the adsorption of MB via prepared Ni/CMC nanocomposite was an endothermic and spontaneous process (Graphical abstract NiO CMC).
Keywords:Nanoparticles; Nanocomposites; Methylene blue; Adsorption kinetics; Dye removal
Introduction
Globally, the rapid development of manufacturing in many fields because of the vast population growth of many pollutants, such as heavy metals, organic and inorganic compounds, is released in the air and water. Due to their harmful to living organisms, the need for contaminant removal has become a challenging mission and necessary [1]. Methylene blue (MB), despite its importance as coloring agents and pharmaceuticals, causes chest pain, restlessness, skin diseases such as cancer and psoriasis, apprehension, allergic dermatitis, and eye burns when exposure directly to large doses [2-4]. Unfortunately, Due to the complex structures of MB that make it difficult to remove. Because of that, increasing attention has been on removing MB from the wastewater. Many techniques have been extensively used for the treatment and removal of dye from waste water, including photo-degradation [5], adsorption [6], coagulation, and flocculation [7], cation exchange [8], and advanced oxidation processes [9]. Remarkably, the adsorption technique has been attracted attention because of its simplicity of design, ease of operation, high-efficiency, and environmentally friendly, which encouraged researchers to synthesize useful materials for this purpose [10]. Many adsorbents were applied to remove the dye, for instance, metal-organic frameworks (MOFs) and activated carbon.
In contrast, the non-renewable sources and high price of activated carbon and the pollution during the preparation process of MOFs are limit their application as adsorbents [11-13]. Many of the literature reports showed that metal nanomaterials effectively remove the MB from solution; furthermore, nanofibrous cellu-lose membranes show the highly efficient adsorbent for removing MB [6,14,15]. Based on recent research, NiO nanoparticles have excellent catalytic results for removing MB. Nevertheless, nickel nanoparticles are unstable and sensitive to air because it must be immobilized onto support materials [16-19]. Moreover, cellulose is an abundant and renewable organic natural polymer and has many interesting properties such as high surface area, good adsorption capability, degradability, biodegradability, and good mechanical. Also, it contains plenty of hydroxyl groups, easily replacing them with other functional groups to improve its performance [20,21]. Carboxymethyl cellulose (CMC) is one of the most important derivatives of modified cellulose obtained through the etherification reaction on C6 hydroxyl groups [22]. Its non-toxicity, high water solubility, marvelous light, and thermal stability have broad applications in an enormous field such as food, pharmaceutical, detergents, and lubricants [23,24]. Numerous and diverse methods are used to prepare NiO nanoparticles and classified into the chemical and physical methods, including sol-gel [25], hydrothermal [26], solvothermal [27], and co-precipitation [28]. The last method is utilized in this work by sodium borohydride as a reducing agent that is efficient, straightforward, cost-effective, and safe because it does not need any toxic chemicals and cruel reduction conditions.
Furthermore, Fe3O4polyoxometalates nanocomposites were synthesized and applied to adsorb the cationic dyes from aqueous solution [29]. In addition, the multiple uses of nanocomposites in environmental fields, they can be used in energy fields such as Ag/ SiO2 Core-shell Nanoparticles were inserted in a TiO2 mesoporous layer extensively to improve the performance of perovskite solar cells [30].
This work aims to synthesize a novel nanocomposite based on carboxymethyl cellulose containing nickel oxide nanoparticles (NiO/CMC) for efficient removal of MB from wastewater. The synthesized nanocomposites will be characterized by Fourier transform infrared spectroscopy (FT-IR), Scanning electron microscopy (SEM), Energy dispersive x-ray spectroscopy (EDX), Transmission electron microscopy (TEM), and X-ray powder diffraction (XRD) techniques. The effects of the first concentration of MB, contact time, nanocomposite concentration, temperature, and pH on the MB degradation outcomes by nanocomposites; moreover, the adsorption kinetics, equilibrium isotherms, and thermodynamic will be investigated.
Materials and Methods
Cellulose powder (C6H10O5)n, nickel nitrate hexahydrate Ni(NO3)2.6H2O (98%), sodium borohydride NaBH4, (98%), monochloroacetic acid C2H3ClO2 (99%), ethanol (99.9%), 2-propanol (99.8%), methylene blue [C16H18ClN3S, WARDS] and sodium hydroxide (98%) were purchased from Sigma-Aldrich US Co. They were used as received without further purification, and all solutions were prepared using distilled water.
Preparation of carboxymethyl cellulose
CMC was prepared according to reported methods [31] as follows: 1mole of cellulose (10gm) was mixed very well by a mechanical stirrer for 10 min with 1 mole of sodium hydroxide (3.08g) in the presence of water: isopropanol 3:3 (v/v) mixture and then 1.5 moles of mono chloroacetic acid (9.64gm) was added with continuous stirring. The reaction mixture was transferred into a thermostatic water bath at 80 ∘C for 3 hrs. The neutralization step was occurred by adding drops of HCl conc. The prepared sample was filtered and washed by a mixture of water/isopropanol 30:70 (v/v) for 24 hrs. Finally, the washed sample was dried in an oven at 70 ∘C for 1 hr. The degree of substitution of the prepared sample was 0.033.
Synthesis of NiO /CMC nanocomposites
The metal nanoparticles in situ cellulose modified surface using sodium borohydride as a reducing agent was carried out according to the reported method [32] as follows: 0.5 g of CMC was mixed well with 50 ml (0.01M) of nickel nitrate hexahydrate salts solution in Ultrasonic bath sonication for 30 min. Subsequently, 1M of NaBH4 was added gradually under stirring with a mechanical stirrer until it changed to black. Finally, the prepared sample was filtered off and washed several times with distilled water to remove the extra NaHB4 and dried in an oven at 60 ∘C for 1 hour. The dried sample was transferred into the Muffle furnace at 300 ∘C for 24 hrs.
Characterizations
Prepared NiO/CMC nanocomposites were confirmed for solid samples using Fourier transform infrared spectroscopy (FT-IR, Agilent Technologies, cary630, Malaysia). The surface morphology and the prepared nanocomposite elemental composition were investigated by scanning electron microscopy coupled with dispersive energy X-ray diffraction (SEM-EDX type JXA-840 an electron probe microanalyzer-JOEL). Particle size diameter and prepared nanocomposite distribution were determined using a transmission electron microscope (TEM ZEISS-EM-10-GERMANY). The crystallinity of prepared composites was measured by X-ray diffraction (XRD, Rigaku, Tokyo, Japan) using Cu-Kα radiation (λ = 0.154 nm) at 40 kV and 30 mA with 2θ range from 5o to 80o.
MB dye adsorption
Methylene blue adsorption was studied according to the reported method [33] as follows: a solution of MB with different concentrations (3,7,11,15 mg/L) were prepared. The different amounts of prepared nanocomposites (2,4,6, and 8mg) and 0.2M NaBH4 were added to each prepared MB solution at different temperatures (25-65 ∘C) for different contact times (0-72 hrs.) with different pH values (2-8). MB’s removal was determined by measuring MB’s concentration before and after treatment with nanocomposite using UV-Vis spectrophotometry (GENESYS 10S UV VIS, Thermo Scientific, Madison) at maximum wavelength λmax= 660 nm. The dye removal percentage was calculated by the equation to follow:
Results and Discussion
FTIR analysis
FTIR spectroscopy is very useful to get information about chemical changes that occurred after chemical treatments. Figure 1a shows the spectra of native cellulose with large bands at 3280 cm-1, 2894 cm-1, and 1428 cm-1, which corresponds to the OH-stretching vibration, C-H stretching vibration, and CH2 bending vibration, respectively. Nevertheless, bands at 1027 cm-1and 892 cm-1 correspond to C-O-C pyranose ring vibration and stretching C-O-C of the β(1→4)-glycosidic linkage between the glucose units, respectively [34]. Figure 1b shows the CMC spectra, and the data display that two broad peaks at 1725 cm-1 and 1628 cm-1 correspond to stretching vibration of OH and C=O of (COOH) group, respectively [35]. Figure 1c shows the IR spectra of NiO-CMC, a peak that related to COOH becomes low intensity and shifted from 1628 cm-1 to 1653 cm-1. On the other hand, a peak for the C-O-C pyranose ring becomes weak, and a characteristic peak has appeared at 457 cm-1, which is assigned to NiO vibration; this means that the coordination between the carboxyl group and Ni metals is occurred [36] (Figure 1).
SEM and EDX analysis
Figure 2 shows the SEM and SEM-EDX spectra of microcrystalline cellulose, CMC, and NiO-CMC nanocomposite. The SEM images clearly show that regular flat shape with a semi-porous surface. NiO nanoparticles are well distributed inside the backbone of the CMC structure without aggregation. These images also show that CMC’s surface becomes rough due to a large deposition of semi-cubic shape nanoparticles with different sizes over the CMC surface, and plenty of NiO nanoparticles are visible with great levelness with the high distribution. SEM-EDX spectral analysis of microcrystalline cellulose, CMC, and NiO-CMC nanocomposite shows distinctive energy peaks at around 5 and 10 keV, which characteristic carbon of native cellulose, and two peaks from 10 and 22 keV, which characteristic of oxygen for CMC. Figure 2c shows the EDX spectral analysis of NiO-CMC nanocomposite. The Figure shows that the distinctive energy peaks around 76 and 80 keV, which characteristic NiO nanoparticles (Figure 2).
TEM analysis
Figures 3 a,b shows TEM images of CMC and NiO-CMC nanocomposite, respectively. The images show that NiO/CMC nanocomposite is a particle with a spherical shape, dark spots, random distribution, and diameter size ranging from 15 to 42nm. Figure 3c shows that the histogram of nanoparticle size distribution on the CMC surface is 15.29% of particles with 28 nm size and 11.76% have 20nm. This confirms the immobilization of nanoparticles onto the CMC surface. Generally, the average size of the particles was 25.80 nm (Figure 3).
XRD analysis
To investigate the materials’ crystal structure and purity, X-ray diffraction (XRD) analysis was used. Figure 4A shows the XRD patterns for CMC, the prominent characteristic peaks were observed in a region of 2θ from at 16.2o , and 22.8o were assigned to (110) and (200) planes of crystalline cellulose [37]. Figure 4B shows the crystallographic behavior of the NiO-CMC nanocomposite. The peaks at 2θ of 35.16, 43.91, 55.34, and 60.80o have been identified as peaks of cubic NiO crystallites, which are corresponding to crystal planes (111), (200), (220) and (311) respectively. The peak observed at 2θo of 30.48o was identified for Ni2O3 (004), according to the standard spectrum (JCPDS, No.73-1519), and no other peaks corresponding to nickel-metal were observed. Moreover, a characteristic peak at 2θ of 25.24o, indicating that the CMC surface’s nickel oxide nanoparticles did not change the CMC’s crystalline structure. Additionally, the average D values of metal oxide nanoparticles were calculated using Scherrer’s formula (3), and it was found that the average diameter of metal oxide nanoparticles is 25 to 45nm (Figure 4).
where D is crystallite size (nm), k is Scherrer constant= 0.89, λ is the X-ray wavelength= 0.15425 nm, β is the full width at half maximum of the peak (FWHM), and θ is the Bragg angle [38].
Degradation of methylene blue
Effect of contact time
The influence of the difference in contact time (0-72 hours) on MB removal percentage by different adsorbents A) cellulose, B) CMC and C) NiO-CMC was investigated at 25 oC, initial concentration of MB solution (3 mg/L), pH 2, adsorbent dose 2.5mg in the presence of (0.2M NaBH4). Figure 5A shows that the removal efficiency percent of MB by cellulose was increased from 1.6 to 4.6 % in the first period and then becomes constant. Furthermore, it can be observed that the MB removal efficiency percent was increased to 6 % in the case used of CMC, as shown in Figure 5B. This is due to many sites were available in the initial period. The longer the contact time, the active site to be limited, and there is a decrease in adsorption (Figure 5).
In comparison, the dye removal efficiency percent was achieved to 99.98 % by increasing the contact hour in the presence of NiOCMC nanocomposite, as can be seen in Figure 5C. This is attributed to the nanoparticles that will accelerate the reduction process of MB by transferring the electrons from BH- 4, which is a (donor) to MB (accepter) [39]. The high removal percentage of the synthesized nanocomposites observed in this study will attract more attention in the future for wastewater treatment.
Effect of initial dye concentration
Figure 6 displays the adsorption capacity q of NiO-CMC nanocomposite at different MB concentration Qt (3, 7, 11 and 15 mg/L) for different contact time (0 -72 hours) at 25 oC, pH 2, adsorbent dose 2.5 mg and 0.5 ml of (0.2M NaBH4). The data show that the adsorption capacity of NiO-CMC gradually increase with increases the dye concentration during the first 1.5 hours until the equilibrium at 4 hours and this is attributed to the plenty sites on the surfaces of nanocomposite then, it is slightly changed because the ions of methylene blue are looking to find available adsorption sites. The adsorption capacity values at 4 hours (9.36, 12.32, 17.6, and 16.52) mg/g for initial concentration MB (3, 7, 11, and 15) mg/L, respectively. When the contact time is more than 4 hours, a little change in adsorption capacity is observed.
Effect of temperature
Figure 7 demonstrates the effect of temperature on adsorption of MB using NiO-CMC nanocomposite. The condition of experiment was initial concentration of MB 3 mg/L, dose = 2.5 mg, for contact time 4 hours, pH 2, and 0.5 ml of (0.2M NaBH4). The data show that the MB adsorption increases with increasing the temperature from 25 to 65 oC and increases the removal efficiency percent from 44 to 90 %. This confirms that the process of MB adsorption by NiO-CMC is endothermic based on the thermodynamic of adsorption data.
Effect of nanocomposite amount
For investigating the impact of the necessary adsorbent amount, various amounts of NiO-CMC nanocomposite from 2 to 8 mg were added to 10 mL of 3 mg/L MB solutions. The results of these experiments are illustrated in Figure 8. This Figure shows the MB removal efficiency percent increase with the increasing adsorbent amount to reach 75 % using 0.008 g of adsorbent. The increase of the available surface for the adsorption process explains how the removal percentage increased from 25 to 75 %. The adsorption capacity decreased from 4.5 to 2.7 mg/g. The fixed amount of the available MB molecules is the limiting factor here. When the amount of adsorbent increased, the removal percent and Qe values were increased, and in amounts of adsorbent greater than 4.5 mg, these values were decreased. This is attributed to the saturation of the adsorbent activated sites takes place [40]. So, for the rest of the experiments, 4.5 mg of adsorbent was used for dye removal (Figure 8).
Effect of pH
pH is an important reason for the adsorption process. It can promote or decrease adsorbent ionization and dye. Figure 9 shows the removal efficiency percent of MB increase with pH increases from 2 to 6 and then becomes almost constant at pH more than 6. This behavior is due to CMC’s active sites carrying a negative charge while the MB carries a positive charge, which causes an electrostatic force between them and attracts many MB cations from the solution. In contrast, at lower pH, the positive charge increases on CMC, then the electronic repulsion takes place with MB cations [41].
Kinetics of adsorption
Figure 10 (A, B) shows the application of adsorption kinetics models pseudo-first-order and pseudo-second-order of MB dye adsorption on NiO-CMC nanocomposite. During the adsorption process, the electrostatic interaction occurred when the MB molecules (cationic) migrated from the aqueous solution to the nanocomposite surface. Regarding all adsorbents, the most generally applicable model for describing the MB dye adsorption process is the pseudo- second-order [42]. In order to find out the adsorption process followed pseudo first order kinetics or pseudo-second-order, the following generalized first pseudo order kinetic equation (4) and pseudo-second-order equation (5) was employed [43].
where Co is the initial concentration and Ct is the residual concentration of MB (mg/L) at a definite time t (min), and k1 is the rate constant for pseudo-first-order (h-1),
where k2 is the rate constant for pseudo-second-order (L/mg.hrs) [44]. S1 summarizes the rate constant values K1, K2 n, and the correlation coefficients, R21 and R21 of MB degradation for pseudo- first-order and pseudo-second-order, respectively. It clarifies that the adsorption of MB onto NiO-CMC followed the pseudo-second- order model based on the correlation coefficients (R22) values, which are close to the unity (R22=0.977, 0.982, 0.969 and 0.992) whereas the values of R2 1 for pseudo-first-order are (0.720, 0.922, 0.854 and 0.966). The values of rate constants were decreased gradually with the increase of MB’s initial concentration from 3 to 15 (mg/L) due to by increasing the concertation of MB, the active sites of nanocomposite become limited by MB molecules. This confirms that the pseudo-second-order satisfactorily describes the best kinetic model for MB’s adsorption by NiO-CMC nanocomposite.
Isotherms of adsorption
To understand the distribution of MB molecules on nanocomposite (liquid-solid) phases at equilibrium, adsorption isotherms are used by analyzed experimental data for the Langmuir and Freundlich models. Langmuir model assumes that the adsorbate molecules MB can be the only adsorption on one active site without interaction between the adsorbent molecules and after equilibrium, there is no supplemental adsorption. It is expressed in equation (6) as follow [45].
where Ce, Qe, qmax, and kL are the equilibrium concentration of MB (mg/L), the amount of MB dye adsorbed by adsorbent (nanocomposite) at equilibrium (mg/g), the theoretical maximum monolayer adsorption capacity of the adsorbent (mg/g) and constant of Langmuir (L/mg), respectively. From the plotting Vs Ce we can determine qmax and KL as shown in S2a. RL is the dimensionless constant separation factor. It is an essential characteristic of this model to predict if the adsorption is favorable or not, and it can be calculated from equation (7)
Where Co is the highest concentration of MB. If RL’s value was between zeros to one, which indicates that the adsorption process is favorable. On contrary, if RL > 1 is unfavorable process while, if RL = is liner. On the other hand, Freundlich is suggested that the multilayer adsorption of adsorbate (MB) on adsorbent surfaces (non-ideal adsorption). The linear equation form of the Freundlich model as following in equation (8) [46]:
where kF and 1/n are the Freundlich constant (L/mg) and the adsorption intensity, respectively. It is necessary to determine values of them from plotting ln Qe Vs Ce as shown in S2b) if the value of 1/n < 1 suggests normal adsorption (Langmuir isotherm), while 1/n > 1 indicates the adsorption process is cooperative.
Based on the S3, which summarized the parameters of tow isotherm models, it was observed that R2 value for the Langmuir model is higher than Freundlich, which equals 0.964 with maximum adsorption capacities 18.52 (mg/g) and RL equal 0.057, which below the unit and this means that, there is a strong correlation between MB molecules with active sites of an adsorbent. Moreover, 1/n was 0.22, which confirms that the adsorption approach of MB on NiOCMC nanocomposite is favorable by homogeneous monolayer.
Thermodynamic of adsorption
Thermodynamics behavior was studied for adsorption of MB onto nanocomposite. The parameter of thermodynamic calculated by van’t Hoffs equation as follow (9)
where Kd, ΔSo, ΔHo, T and R are the equilibrium rate constant (L/g), the standard entropy (ΔSo) (J/mol.K), the standard enthalpy (J/mol), temperature(K) and gas constant (J/K.mol), respectively and equation (10) to calculate the standard Gibbs free energy ΔGo (J/mol).
From the plot of lnKd Vs 1/T ΔSo and ΔHo values can be obtained by intercept and slop respectively, as shown in S4 [38] (Taher, Rohendi, Mohadi, & Lesbani, 2018). All parameter values are listed in S5. It was evident that the ΔSo value was positive (19.14 kJ/mol.K), which indicates that the randomness of the solid (nanocomposite) −solution (MB) interface increased when the dye molecules become close to the active sites of nanocomposite during the adsorption process [15]. The ΔHo values were positive (5.54 kJ/mol), which means MB’s adsorption onto nanocomposite is an endothermic process. All values of ΔGo are negative, and ΔGo values decrease from -2.82 to -10.04 (kJ/mol) with an increase of adsorption temperatures from 298 to 338 (K). This indicates that the adsorption process is spontaneous at various temperatures.
Conclusions
Nickle oxide-carboxymethyl cellulose nanocomposite has been successfully synthesized and applied to remove methylene blue from aqueous solution. The synthesized nanocomposite was characterized using FT-IR, SEM, EDX, TEM, and XRD, and the obtained data showed that NiO nanoparticles were chemically bonded and well distributed inside the backbone of the CMC structure without aggregation. Furthermore, NiO/CMC nanocomposite has appeared as a particle with a spherical shape, dark spots, random distribution, and diameter size ranged from 15 to 42nm. Also, XRD data showed that the CMC surface’s nickel oxide nanoparticles did not change the crystalline structure of the CMC. The Langmuir criterion for MB removal (K) indicates that the Nickle oxide-carboxymethyl cellulose nanocomposite was extremely efficient in removing MB with low sorption energy. According to Langmuir isotherm, the most significant sorption capacity was found 3.03 (mg/g) at 25 oC. The kinetic data showed that the process was a pseudo-second-order process, and the isotherm model was fitted firmly. Thermodynamic parameters showed that ΔSo and ΔHo values were positive and all values of ΔGo were negative, and ΔGo values decreased with increasing of adsorption temperatures from 298 K to 338 K, which indicated that the adsorption of MB by nanocomposite was endothermic and spontaneous processes.
To read more about this article....Open access Journal of Textile Science & Fashion Technology
Please follow the URL to access more information about this article
To know more about our Journals...Iris Publishers
No comments:
Post a Comment